o:33312 Overview of research results of the influence of grain size on beams of different structures of concrete by interpolation en Abstract: In order to research the influence of the dimensions there have been used the samples of slotted beams on two supports and loaded by force capacity of P = 200 kN and the sensitivity of 100 N fractured (load cell), in the middle, deformations were measured at the point of load and the top of each slot of 50 mm with the sensitivity instrument of 100x10-6 mm LVDT (Tokyo Sokki Kenkyujo Co.SDP-50C). During load all deformations are directly stored with the data logger (30 channels Bucem) that is constantly connected to the computer. The thickness of all samples is constant t = 4 cm and the other two dimensions of height h and length L are changed proportionally. For testing are used three different sizes of the beams and from each sizes are used the three samples. To a mixture of concrete were used two aggregate fractions. A large fraction is 4.76 to 10 mm, smaller fraction is 3 to 4,76 mm. First, sand is put into a mixer, followed by gravel and cement in the dry state and this is going to be mixed for about 2 minutes, after that, the water is added and mixing is going to be carried out for about 2 minutes. From the same samples were set aside the 3 samples in the molds of cylindrical forms with a diameter of 150 mm and a height of 300 mm to determine the brand of concrete. There was used the portland cement (350). Keywords: impact on size, compressive strength of concrete, fracture, interpolation, beam. 1552101 1583-0691 1552099 10.15660/AUOFMTE.2014-2.3029 2024-03-28T07:09:59.725Z 44 no 46 Nazim Manić Državni univerzitet u Novom Pazaru 0000-0001-8346-8255 Mirsad Tarić person Veis Šerifi person Žana Džubur person application/pdf 359995 https://phaidrabg.bg.ac.rs/o:33312 no yes 1 70 92000001 20A01 Annals of the university of Oradea, Fascicle of Management and Technological Engineering 23 2 30 37 2014